ANALISA VARIASI SUHU DAN WAKTU PERAWATAN TERHADAP KUAT TEKAN BETON GEOPOLIMER
View through CrossRef
<p><em>The increase in cement production has a negative impact on the environment, so innovation in the use of concrete adhesives is needed, one of which is by utilizing fly ash waste. In order to react to form polymer bonds, fly ash requires the addition of an activator solution in the form of Sodium Hydroxide (NaOH) and Sodium Silicate (Na2SiO3). At cold temperatures, the hydration process and initial strength of geopolymer concrete will have difficulty being achieved optimally. So additional heat with high temperatures is needed during curing to increase the compressive strength of geopolymer concrete. This study aims to analyze the temperature and curing time on the compressive strength of geopolymer concrete. The research method is an experimental study in the Laboratory with a ratio of aggregate: binder of 65%: 35%, coarse aggregate: fine aggregate of 60%: 40%, alkali: fly ash of 38%: 62%, NaOH: Na2SiO3 of 1: 2, superplasticizer 2%, and activator molarity 12 M. The variations in temperature and curing time used were at temperatures of 60 </em><em>℃</em><em> and 90 </em><em>℃</em><em> for 6 hours, 12 jams and 24 hours. Test objects in the form of cylinders measuring 200</em><em>×</em><em>100 mm as many as 18 samples. The test objects will be tested for compressive strength after 28 days. The results of the study obtained the highest compressive strength value at a variation of 90</em><em>℃</em><em> for 24 hours of 17.92 MPa and the lowest compressive strength value at a variation of 60</em><em>℃</em><em> for 6 hours of 10.19 MPa. Based on the results of the study, it was concluded that the higher the curing temperature and the longer the curing time can increase the compressive strength of geopolymer concrete. For further research, it is recommended to vary the curing temperature above 90</em><em>℃</em><em>, the curing time above 24 hours and reduce the amount of air in the concrete mixture.</em><strong> </strong></p><p><strong><em>Keywords</em></strong><strong><em>:</em></strong><em> <em>compressive strength; curing time; fly ash; geopolymer concrete; temperature time</em></em><em></em></p>
Universitas Sebelas Maret
Title: ANALISA VARIASI SUHU DAN WAKTU PERAWATAN TERHADAP KUAT TEKAN BETON GEOPOLIMER
Description:
<p><em>The increase in cement production has a negative impact on the environment, so innovation in the use of concrete adhesives is needed, one of which is by utilizing fly ash waste.
In order to react to form polymer bonds, fly ash requires the addition of an activator solution in the form of Sodium Hydroxide (NaOH) and Sodium Silicate (Na2SiO3).
At cold temperatures, the hydration process and initial strength of geopolymer concrete will have difficulty being achieved optimally.
So additional heat with high temperatures is needed during curing to increase the compressive strength of geopolymer concrete.
This study aims to analyze the temperature and curing time on the compressive strength of geopolymer concrete.
The research method is an experimental study in the Laboratory with a ratio of aggregate: binder of 65%: 35%, coarse aggregate: fine aggregate of 60%: 40%, alkali: fly ash of 38%: 62%, NaOH: Na2SiO3 of 1: 2, superplasticizer 2%, and activator molarity 12 M.
The variations in temperature and curing time used were at temperatures of 60 </em><em>℃</em><em> and 90 </em><em>℃</em><em> for 6 hours, 12 jams and 24 hours.
Test objects in the form of cylinders measuring 200</em><em>×</em><em>100 mm as many as 18 samples.
The test objects will be tested for compressive strength after 28 days.
The results of the study obtained the highest compressive strength value at a variation of 90</em><em>℃</em><em> for 24 hours of 17.
92 MPa and the lowest compressive strength value at a variation of 60</em><em>℃</em><em> for 6 hours of 10.
19 MPa.
Based on the results of the study, it was concluded that the higher the curing temperature and the longer the curing time can increase the compressive strength of geopolymer concrete.
For further research, it is recommended to vary the curing temperature above 90</em><em>℃</em><em>, the curing time above 24 hours and reduce the amount of air in the concrete mixture.
</em><strong> </strong></p><p><strong><em>Keywords</em></strong><strong><em>:</em></strong><em> <em>compressive strength; curing time; fly ash; geopolymer concrete; temperature time</em></em><em></em></p>.
Related Results
Studi Karakteristik Kuat Tekan Beton Geopolimer Berbahan Dasar Abu Sekam Padi
Studi Karakteristik Kuat Tekan Beton Geopolimer Berbahan Dasar Abu Sekam Padi
Beton geopolimer menjadikan alternatif ramah lingkungan bagi beton konvensional karena memiliki potensi untuk mengurangi emisi karbon. Abu sekam padi yang merupakan limbah pertania...
ANALISIS PENURUNAN MUTU BETON STRUKTURAL AKIBAT PENGARUH AIR LAUT PADA MASA PEMELIHARAAN
ANALISIS PENURUNAN MUTU BETON STRUKTURAL AKIBAT PENGARUH AIR LAUT PADA MASA PEMELIHARAAN
Air laut memiliki kandungan garam yang tinggi yang dapat menggerogoti kekuatan dan keawetan beton. Hal ini disebabkan klorida yang terdapat pada air laut yang merupakan garam yang ...
Studi Pemanfaatan Limbah Serat Gergaji Kayu dan Limbah Kertas Sebagai Campuran Beton Ringan
Studi Pemanfaatan Limbah Serat Gergaji Kayu dan Limbah Kertas Sebagai Campuran Beton Ringan
Limbah sering digunakan sebagai bahan untuk berbagai keperluan, termasuk dalam rekayasa bahan bangunan. Salah satu jenis limbah yang masih jarang diteliti sebagai campuran dalam pe...
ANALISIS KUAT TARIK BELAH BETON PADA STANDAR KUAT TEKAN K.250 DENGAN MENGGUNAKAN LIMBAH PECAHAN BETON SEBAGAI PENGGANTI AGREGAT KASAR
ANALISIS KUAT TARIK BELAH BETON PADA STANDAR KUAT TEKAN K.250 DENGAN MENGGUNAKAN LIMBAH PECAHAN BETON SEBAGAI PENGGANTI AGREGAT KASAR
Beton merupakan bahan konstruksi yang sangat penting dan paling dominan digunakan pada struktur bangunan. Beton sangat diminati karena bahan ini merupakan bahan konstruksi yang mem...
Pengaruh Nilai Abrasi Limbah Beton (Recycle) pada Pembuatan Beton Normal
Pengaruh Nilai Abrasi Limbah Beton (Recycle) pada Pembuatan Beton Normal
Beton merupakan material konstruksi yang saat ini banyak digunakan dalam berbagai bagian bangunan yang kita temui selama proses pembangunan, seperti pada gedung, jalan, dan jembata...
Pengaruh Serat Baja Canai Dingin Bergelombang Terhadap Kekuatan Tekan Dan Lentur Beton
Pengaruh Serat Baja Canai Dingin Bergelombang Terhadap Kekuatan Tekan Dan Lentur Beton
Beton merupakan material konstruksi yang bersifat getas. Kombinasinya dengan baja pada material beton bertulang menjadikan material beton yang getas getas menjadi daktail. Pada bet...
PENGARUH PENGGUNAAN VARIASI PH AIR TERHDAPA KUAT TEKAN BETON NORMAL
PENGARUH PENGGUNAAN VARIASI PH AIR TERHDAPA KUAT TEKAN BETON NORMAL
Dalam pembuatan betonair sangat diperlukan untuk memicu proses kimiawi semen, membasahi agregat halus, dan memberikan kemudahan dalam pekerjaan beton. Pada dasarnya air yang diguna...
EFEK PERAWATAN TERHADAP KARAKTERISTIK BETON GEOPOLIMER
EFEK PERAWATAN TERHADAP KARAKTERISTIK BETON GEOPOLIMER
Geopolymer concrete is a kind of concrete that does not use portland cement as binder but utilizes natural material that contents silica as fly ash, rice husk ash, etcetera.The use...