ANALISIS KEKERASAN BAJA S45C HASIL HARDENING DENGAN VARIASI MEDIA PENDINGIN
View through CrossRef
Steel has good mechanical properties compared with the other materials, that
is strength, hardness, rigidity, etc. Specially the steel hardness can be increased by
heat treatment (Hardening).
The purpose of this research is to obtain information about hardness of S45C
steel after hardening by variation of cooling media.
This research were used Ø 25 mm x 10 mm S45C steel, Hardened by
variation of cooling media and then they were tested by Rockwell Harness Test.
The result showed that the hardness of S45C steel after hardening increased
from about 15 HRC (before hardening) to 71.89 HRC (Brane quenching), 68.22
HRC (Water quenching), 64.67 HRC (Water + Soluble oil quenching) and 56.89
HRC (Oil quenching), but for the range were opposite to 3.84 HRC (Brane
quenching), 4.24 HRC ( Water quenching), 4.22 HRC (Water + Soluble oil
quenching) and 5.65 HRC (Oil quenching)
Center for Journal Management and Publication, Lambung Mangkurat University
Title: ANALISIS KEKERASAN BAJA S45C HASIL HARDENING DENGAN VARIASI MEDIA PENDINGIN
Description:
Steel has good mechanical properties compared with the other materials, that
is strength, hardness, rigidity, etc.
Specially the steel hardness can be increased by
heat treatment (Hardening).
The purpose of this research is to obtain information about hardness of S45C
steel after hardening by variation of cooling media.
This research were used Ø 25 mm x 10 mm S45C steel, Hardened by
variation of cooling media and then they were tested by Rockwell Harness Test.
The result showed that the hardness of S45C steel after hardening increased
from about 15 HRC (before hardening) to 71.
89 HRC (Brane quenching), 68.
22
HRC (Water quenching), 64.
67 HRC (Water + Soluble oil quenching) and 56.
89
HRC (Oil quenching), but for the range were opposite to 3.
84 HRC (Brane
quenching), 4.
24 HRC ( Water quenching), 4.
22 HRC (Water + Soluble oil
quenching) and 5.
65 HRC (Oil quenching).
Related Results
Evaluasi Kemampuan Sistem Pendingin Reaktor Setelah Revitalisasi Menara Pendingin
Evaluasi Kemampuan Sistem Pendingin Reaktor Setelah Revitalisasi Menara Pendingin
Evaluasi Kemampuan Sistem Pendingin Reaktor Setelah Revitalisasi Menara Pendingin. Sistem pendingin RSG-GAS terdiri dari sistem pendingin primer dan sekunder. Sistem pendingin prim...
ANALISA VARIASI VISCOSITAS PELUMAS PADA PROSES QUENCHING TERHADAP SIFAT MEKANIK BAJA AISI 1045
ANALISA VARIASI VISCOSITAS PELUMAS PADA PROSES QUENCHING TERHADAP SIFAT MEKANIK BAJA AISI 1045
Baja AISI 1045 memiliki kadar komposisi kandungan karbon sekitar 0,43 sampai dengan 0,50. Aplikasi baja AISI 1045[1], [2]. banyak digunakan dalam bidang otomotif. seperti pembuatan...
ANALISIS SIFAT MEKANIS BAJA St.60 HASIL PENGELASAN FRICTION WELDING DENGAN VARIASI PENDINGIN
ANALISIS SIFAT MEKANIS BAJA St.60 HASIL PENGELASAN FRICTION WELDING DENGAN VARIASI PENDINGIN
Banyaknya komponen dalam industri manufaktur memerlukan penggunaan teknik pengelasan yang efektif dan efisien. Pengelasan gesekan adalah metode penyambungan benda padat di mana laj...
Kajian Eksperimental Proses Las Smaw Pada Logam Baja Jis S45C Dengan Variasi Elektroda Terhadap Sifat Mekanis
Kajian Eksperimental Proses Las Smaw Pada Logam Baja Jis S45C Dengan Variasi Elektroda Terhadap Sifat Mekanis
Penelitian ini bertujuan untuk mengetahui pengaruh variasi arus las SMAW (Shielded Metal Arc Welding) terhadap sifat mekanis pada sambungan las baja JIS S45C dengan variasi elektro...
Analisis Struktur Mikro pada Baja St 60 Hasil Perlakuan Hardening dengan Menggunakan Variasi Media Pendingin
Analisis Struktur Mikro pada Baja St 60 Hasil Perlakuan Hardening dengan Menggunakan Variasi Media Pendingin
Penelitian ini bertujuan untuk menganalisis struktur mikro baja ST 60 setelah perlakuan pengerasan (hardening) dengan menggunakan variasi media pendingin. Baja ST 60 dipilih karena...
PENGARUH MEDIA PENDINGIN PADA BAJA EKSTRA KNL MELALUI PROSES HARDENING PADA SUHU 1020°C
PENGARUH MEDIA PENDINGIN PADA BAJA EKSTRA KNL MELALUI PROSES HARDENING PADA SUHU 1020°C
Pada proses produksi khususnya di proses pemesinan untuk membentuk sebuah produk perlu memahami material yang harus dibentuk. Dalam hal ini material yang dipakai yaitu Baja perkak...
Analisis Kerusakan Expansion Valve pada Mesin Pendingin Refrigerator di MT. Gas One
Analisis Kerusakan Expansion Valve pada Mesin Pendingin Refrigerator di MT. Gas One
A refrigerator cooling machine is an auxiliary machinery designed to generate a temperature that serves as a coolant for food ingredients. Among its components, the expansion valve...
Baja dan Aplikasinya
Baja dan Aplikasinya
Baja dan paduannya adalah material Teknik yang paling banyak pemakaiannya dalam industri manufaktur mulai dari industri rumah tangga sampai industri berat dan militer. Baja dibuat ...