PENGARUH SERAT BAJA (DRAMIX) TERHADAP KUAT LENTUR PADA ROLLER COMPACTED CONCRETE (RCC)
View through CrossRef
ABSTRACTRigid pavement for highways in Indonesia started as an alternative for road pavement. Roller compacted concrete (RCC) is one type of dry concrete mixture with low water cement ratio (slump <5 cm). The RCC spreading is the same as the asphalt concrete pavement that uses the finisher and is compacted using a roller. This research uses RCC mix design with cement water factor value 0,25. Additional silicafume materials of 10%, superplasticizer 2.4%, and steel fiber (dramix) with variations of 0.5% and 1%. RCC Compaction using standard proctor tools. Testing of bending forces and compression of concrete in 1 day and 28 days. The result of research of RCC variation of 0.5% steel fiber and 1 day old concrete obtained Flexural Strength of 4,2 MPa while 28 days concrete gained Flexural Strength of 5,7 MPa. The variation of 1% steel fiber 1 day concrete obtained 3.4 MPa Flexural Strength, while the 28 days concrete obtained 6.1 MPa Flexural Strength.Keywords: Roller Compacted Concrete (RCC), Steel Fiber (dramix), Flexural Strength ABSTRAKPerkerasan kaku di Indonesia semakin banyak digunakan sebagai alternatif perkerasan jalan raya. Roller Compacted Concrete (RCC) atau beton padat giling (BPG) merupakan salah satu jenis campuran beton kering dengan faktor air semen (FAS) yang rendah (slump <5 cm). Penghamparan RCC sama seperti penghamparan perkerasan beton aspal yang menggunakan finisher dan dipadatkan menggunakan roller. Kajian ini menggunakan mix design RCC dengan nilai faktor air semen 0,25. Bahan tambah silicafume sebesar 10%, superplasticizer 2,4%, dan serat baja (dramix) dengan variasi 0,5% dan 1%. Pemadatan RCC menggunakan alat standar proctor. Pengujian kuat lentur pada beton umur 1 hari dan 28 hari. Hasil kajian RCC variasi serat baja 0,5% beton umur 1 hari diperoleh kuat lentur 4,2 MPa, sedangkan beton umur 28 hari diperoleh kuat lentur 5,7 MPa. Variasi serat baja 1% beton umur 1 hari diperoleh kuat lentur 3,4 MPa, sedangkan beton umur 28 hari diperoleh kuat lentur 6,1 MPa. Kata kunci: Roller Compacted Concrete (RCC), Beton Padat Giling (BPG), Serat baja (dramix), Kuat lentur
Universitas Negeri Yogyakarta
Title: PENGARUH SERAT BAJA (DRAMIX) TERHADAP KUAT LENTUR PADA ROLLER COMPACTED CONCRETE (RCC)
Description:
ABSTRACTRigid pavement for highways in Indonesia started as an alternative for road pavement.
Roller compacted concrete (RCC) is one type of dry concrete mixture with low water cement ratio (slump <5 cm).
The RCC spreading is the same as the asphalt concrete pavement that uses the finisher and is compacted using a roller.
This research uses RCC mix design with cement water factor value 0,25.
Additional silicafume materials of 10%, superplasticizer 2.
4%, and steel fiber (dramix) with variations of 0.
5% and 1%.
RCC Compaction using standard proctor tools.
Testing of bending forces and compression of concrete in 1 day and 28 days.
The result of research of RCC variation of 0.
5% steel fiber and 1 day old concrete obtained Flexural Strength of 4,2 MPa while 28 days concrete gained Flexural Strength of 5,7 MPa.
The variation of 1% steel fiber 1 day concrete obtained 3.
4 MPa Flexural Strength, while the 28 days concrete obtained 6.
1 MPa Flexural Strength.
Keywords: Roller Compacted Concrete (RCC), Steel Fiber (dramix), Flexural Strength ABSTRAKPerkerasan kaku di Indonesia semakin banyak digunakan sebagai alternatif perkerasan jalan raya.
Roller Compacted Concrete (RCC) atau beton padat giling (BPG) merupakan salah satu jenis campuran beton kering dengan faktor air semen (FAS) yang rendah (slump <5 cm).
Penghamparan RCC sama seperti penghamparan perkerasan beton aspal yang menggunakan finisher dan dipadatkan menggunakan roller.
Kajian ini menggunakan mix design RCC dengan nilai faktor air semen 0,25.
Bahan tambah silicafume sebesar 10%, superplasticizer 2,4%, dan serat baja (dramix) dengan variasi 0,5% dan 1%.
Pemadatan RCC menggunakan alat standar proctor.
Pengujian kuat lentur pada beton umur 1 hari dan 28 hari.
Hasil kajian RCC variasi serat baja 0,5% beton umur 1 hari diperoleh kuat lentur 4,2 MPa, sedangkan beton umur 28 hari diperoleh kuat lentur 5,7 MPa.
Variasi serat baja 1% beton umur 1 hari diperoleh kuat lentur 3,4 MPa, sedangkan beton umur 28 hari diperoleh kuat lentur 6,1 MPa.
Kata kunci: Roller Compacted Concrete (RCC), Beton Padat Giling (BPG), Serat baja (dramix), Kuat lentur .
Related Results
Pengaruh Serat Baja Canai Dingin Bergelombang Terhadap Kekuatan Tekan Dan Lentur Beton
Pengaruh Serat Baja Canai Dingin Bergelombang Terhadap Kekuatan Tekan Dan Lentur Beton
Beton merupakan material konstruksi yang bersifat getas. Kombinasinya dengan baja pada material beton bertulang menjadikan material beton yang getas getas menjadi daktail. Pada bet...
PENGARUH SERAT LIMBAH KALENG ALUMINIUM PADA CAMPURAN BETON TERHADAP KARAKTERISTIK MEKANIS BETON
PENGARUH SERAT LIMBAH KALENG ALUMINIUM PADA CAMPURAN BETON TERHADAP KARAKTERISTIK MEKANIS BETON
Sampah merupakan limbah padat yang memiliki potensi untuk dapat diolah kembali, sehingga memiliki nilai ekonomis. Sampah dengan konsentrasi dan kuantitas yang tinggi tentunya akan ...
Pengaruh Arah Serat Terhadap Kekuatan Lentur Komposit Hybrid Serat Daun Nanas dan Lidah Mertua
Pengaruh Arah Serat Terhadap Kekuatan Lentur Komposit Hybrid Serat Daun Nanas dan Lidah Mertua
Material komposit berpenguat serat alam merupakan alternatif ramah lingkungan dalam pengembangan material struktur ringan. Serat alam daun nanas (PALF) dan serat lidah mertua (Sans...
Kekuatan Tarik Dan Lentur Komposit Poliester Berpenguat Serat Cordyline Australis (Daun Praksok) Dengan Perlakuan Air Laut
Kekuatan Tarik Dan Lentur Komposit Poliester Berpenguat Serat Cordyline Australis (Daun Praksok) Dengan Perlakuan Air Laut
Komposit didesain untuk menjadi material alternatif pengganti logam. Unsur utama dari komposit adalah serat dan matriks, serat adalah sumber dari kekuatan dan kekakuan pada komposi...
PERAN TATA KELOLA PERUSAHAAN DALAM MEMODERASI PENGARUH IMPLEMANTASI GREEN ACCOUNTING, CORPORATE SOCIAL RESPONSIBILITY DAN FIRM SIZE TERHADAP KINERJA KEUANGAN
PERAN TATA KELOLA PERUSAHAAN DALAM MEMODERASI PENGARUH IMPLEMANTASI GREEN ACCOUNTING, CORPORATE SOCIAL RESPONSIBILITY DAN FIRM SIZE TERHADAP KINERJA KEUANGAN
This study examines the role of corporate governance in moderating the influence of green accounting disclosure, corporate social responsibility (CSR), and firm size on the financi...
ANALISIS PENURUNAN MUTU BETON STRUKTURAL AKIBAT PENGARUH AIR LAUT PADA MASA PEMELIHARAAN
ANALISIS PENURUNAN MUTU BETON STRUKTURAL AKIBAT PENGARUH AIR LAUT PADA MASA PEMELIHARAAN
Air laut memiliki kandungan garam yang tinggi yang dapat menggerogoti kekuatan dan keawetan beton. Hal ini disebabkan klorida yang terdapat pada air laut yang merupakan garam yang ...
SISTEM KEPENGARANGAN DALAM SERAT-SERAT WULANG PAKUBUWONO IX
SISTEM KEPENGARANGAN DALAM SERAT-SERAT WULANG PAKUBUWONO IX
Penelitian ini bertujuan mendeskripsikan sistem kepengarangan dalam serat-serat wulang Pakubuwono (PB) IX. Data penelitian berupa kata dan kalimat yang menunjukkan sistem kepengara...
SERAT ALAM SEBAGAI BAHAN KOMPOSIT RAMAH LINGKUNGAN
SERAT ALAM SEBAGAI BAHAN KOMPOSIT RAMAH LINGKUNGAN
Serat dalam material diartikan sebagai penguat dimana serat memiliki ukuran yang kecil namun memiliki fleksibilitas yang baik serta kekuatan dalam pembebanan yang tinggi. Dalam seg...