Compositional Analysis of Longshan Period Pottery and Ceramic Raw Materials in the Yongcheng Region, Henan Province

This study systematically analyzes the composition and microstructure of Neolithic pottery unearthed from the Dazhuzhuang, Likou, and Biting Sites in the Yongcheng District using techniques such as X-ray fluorescence spectroscopy (XRF), X-ray diffraction (XRD), infrared spectroscopy (IR), and scanning electron microscopy with energy-dispersive spectroscopy (SEM-EDS). The results show that although the raw materials for pottery at the three sites were likely sourced from nearby ancient soil layers, significant differences in chemical composition and manufacturing techniques are evident. Pottery from the Dazhuzhuang Site is mainly composed of argillaceous gray pottery, with relatively loose raw material selection and a wide fluctuation in SiO2 content (64.98–71.07%), reflecting diversity in raw material sources. At the Likou Site, argillaceous black pottery predominates, characterized by higher Al2O3 content (17.78%) and significant fluctuations in CaO content (1.46–2.22%), suggesting the addition of calcareous fluxes and the adoption of standardized manufacturing techniques. Pottery from the Biting Site mainly consists of argillaceous gray pottery, showing higher Al2O3 content (17.36%), stable SiO2 content (65.19–69.01%), and the lowest CaO content (0.84–1.81%). The microstructural analysis further reveals that the black pottery (from the Likou Site) displays dense vitrified regions and localized iron enrichment. In contrast, the gray pottery (from the Dazhuzhuang and Biting Sites) shows clay platelet structures and vessel-type-specific differences in porosity. This research provides important scientific evidence for understanding raw material selection, manufacturing techniques, and regional cultural interactions in the Yongcheng area during the Longshan Culture period.