Pengaruh Oleamida Terhadap Karakteristik Pematangan Karet Alam Terisi Silika
View through CrossRef
The purpose of this study was as a feasibility study of the utilization of oleamide as a new additive for natural rubber (NR) filled with silica using the semi-efficient vulcanization system. Silica fillers used as much as 30 parts per hundred parts rubber (phr). Oleamide was obtained from the synthesis of oleic acid with urea. Oleamide was inserted into the silica filled NR compounds with the varied composition of 0.0 phr; 2.0 phr; 4.0 phr; 6.0 phr, and 8.0 phr. The influence of oleamide on the curing characteristic of the silica filled NR compounds was observed. It was obtained that the oleamide functions as a curative and also a plasticizer. The greater the levels of oleamide added, the shorter the scorch time and optimum curing time were. Oleamide also decreased the minimum torque with addition up to 8.0 phr. The greater the levels of oleamide was, the lower the minimum torque was. Oleamide also increased the maximum torque and torque difference of the silica-filled NR composites at the addition of 2.0 phr. The 2.0 phr was the optimum composition of the oleamide.
Title: Pengaruh Oleamida Terhadap Karakteristik Pematangan Karet Alam Terisi Silika
Description:
The purpose of this study was as a feasibility study of the utilization of oleamide as a new additive for natural rubber (NR) filled with silica using the semi-efficient vulcanization system.
Silica fillers used as much as 30 parts per hundred parts rubber (phr).
Oleamide was obtained from the synthesis of oleic acid with urea.
Oleamide was inserted into the silica filled NR compounds with the varied composition of 0.
0 phr; 2.
0 phr; 4.
0 phr; 6.
0 phr, and 8.
0 phr.
The influence of oleamide on the curing characteristic of the silica filled NR compounds was observed.
It was obtained that the oleamide functions as a curative and also a plasticizer.
The greater the levels of oleamide added, the shorter the scorch time and optimum curing time were.
Oleamide also decreased the minimum torque with addition up to 8.
0 phr.
The greater the levels of oleamide was, the lower the minimum torque was.
Oleamide also increased the maximum torque and torque difference of the silica-filled NR composites at the addition of 2.
0 phr.
The 2.
0 phr was the optimum composition of the oleamide.
Related Results
PERAN TATA KELOLA PERUSAHAAN DALAM MEMODERASI PENGARUH IMPLEMANTASI GREEN ACCOUNTING, CORPORATE SOCIAL RESPONSIBILITY DAN FIRM SIZE TERHADAP KINERJA KEUANGAN
PERAN TATA KELOLA PERUSAHAAN DALAM MEMODERASI PENGARUH IMPLEMANTASI GREEN ACCOUNTING, CORPORATE SOCIAL RESPONSIBILITY DAN FIRM SIZE TERHADAP KINERJA KEUANGAN
This study examines the role of corporate governance in moderating the influence of green accounting disclosure, corporate social responsibility (CSR), and firm size on the financi...
RANCANG BANGUN RUBBER DAMPER PADA LORI INSPEKSI ELEKTRIK
RANCANG BANGUN RUBBER DAMPER PADA LORI INSPEKSI ELEKTRIK
Sistem suspensi merupakan komponen penting dalam kendaraan, karena berfungsi sebagai peredam getaran bagi kendaraan ketika dikendarai oleh penggunanya. Ada beberapa jenis sistem su...
ANALISIS PERKEMBANGAN PASAR KARET REMAH SIR Analysis of Crumb Rubber SIR Market Developments
ANALISIS PERKEMBANGAN PASAR KARET REMAH SIR Analysis of Crumb Rubber SIR Market Developments
Karet merupakan salah satu komoditas penting di Indonesia. Sebagian besar produksi barang setengah jadi karet Indonesia pada saat ini berupa karet remah SIR khususnya SIR 20. Revie...
PEMANFAATAN BIJI KARET SEBAGAI PRODUK OLAHAN EMPING
PEMANFAATAN BIJI KARET SEBAGAI PRODUK OLAHAN EMPING
Banjarbaru, khususnya daerah kelurahan Cempaka merupakan salah satu daerah penghasil karet di Kalimantan Selatan. Kebanyakan pertanian karet di daerah tersebut merupakan milik pero...
Studi Terhadap Potensi Campuran Abu Kulit Kakao dan Serbuk Cangkang Telur Sebagai Pengganti Pasir Silika Terhadap Kekuatan Tekan Bata Ringan
Studi Terhadap Potensi Campuran Abu Kulit Kakao dan Serbuk Cangkang Telur Sebagai Pengganti Pasir Silika Terhadap Kekuatan Tekan Bata Ringan
Salah satu bahan penyusun utama bata ringan kategori CLC (Cellular Lightweight Concrete) adalah Silika. Namun proses pembuatan bata ini relatif sangat mahal, karena untuk mendapatk...
Nilai Tukar Petani Karet di Desa Penanggoan Duren Kecamatan Tulung Selapan Kabupaten Ogan Komering Ilir OKI
Nilai Tukar Petani Karet di Desa Penanggoan Duren Kecamatan Tulung Selapan Kabupaten Ogan Komering Ilir OKI
Penelitian ini bertujuan untuk mengetahui Berapa nilai tukar petani (NTP) karet di Desa Penanggoan Duren Kecamatan Tulung Selapan Kabupaten Ogan Komering Ilir dan Berapa tingkat pe...
Sintesis Komposit Fiber-Silika dari Abu Sekam Padi dan Pulp dengan Metanol
Sintesis Komposit Fiber-Silika dari Abu Sekam Padi dan Pulp dengan Metanol
Komposit merupakan suatu jenis bahan baru hasil rekayasa yang terdiri dari dua atau lebihbahan dimana sifat masing – masing bahan berbeda atau sama lainnya. Saat ini banyakdikemban...
PERBEDAAN PENGARUH LATIHAN MENENDANG MENGGUNAKAN BENDING DAN MENENDANG MENGGUNAKAN KARET TERHADAP POWER OTOT TUNGKAI DAN LONG PASSING SEPAKBOLA PADA USIA 13-14 TAHUN SEKOLAH SEPAKBOLA KLUMPANG PUTRA
PERBEDAAN PENGARUH LATIHAN MENENDANG MENGGUNAKAN BENDING DAN MENENDANG MENGGUNAKAN KARET TERHADAP POWER OTOT TUNGKAI DAN LONG PASSING SEPAKBOLA PADA USIA 13-14 TAHUN SEKOLAH SEPAKBOLA KLUMPANG PUTRA
Tujuan penelitian untuk mengetahui perbedaan pengaruh latihan menendang menggunakan bending dan menendang menggunakan karet terhadap power otot tungkai dan long passing sepakbola p...