Enhancing Polysulfone Mixed-Matrix Membranes with Amine-Functionalized Graphene Oxide for Air Dehumidification and Water Treatment

Porous low-pressure membranes have been used as active membranes in water treatment and as support for thin-film composite membranes used in water desalination and gas separation applications. In this article, microfiltration polysulfone (PSf)mixed-matrix membranes (MMM) containing amine-functionalized graphene oxide (GO-NH2) were fabricated via a phase inversion process and characterized using XPS, SEM, AFM, DMA, XRD, and contact angle measurements. The effect of GO-NH2 concentration on membrane morphology, hydrophilicity, mechanical properties, and oil–water separation performance was analyzed. Significant enhancements in membrane hydrophilicity, porosity, mechanical properties, permeability, and selectivity were achieved at very low GO-NH2 concentrations (0.05–0.2 wt.%). In particular, the water permeability of the membrane containing 0.2 wt.% GO-NH2 was 92% higher than the pure PSf membrane, and the oil rejection reached 95.6% compared to 91.7% for the pure PSf membrane. The membrane stiffness was also increased by 98% compared to the pure PSf membrane. Importantly, the antifouling characteristics of the PSf-GO-NH2 MMMs were significantly improved. When filtering 100 ppm bovine serum albumin (BSA) solution, the PSf-GO-NH2 MMMs demonstrated a slower flux decline and an impressive flux recovery after washing. Notably, the control membrane showed a flux recovery of only 69%, while the membrane with 0.2 wt.% GO-NH2 demonstrated an exceptional flux recovery of 88%. Furthermore, the membranes exhibited enhanced humidity removal performance, with a permeance increase from 13,710 to 16,408. These results indicate that the PSf-GO-NH2 MMM is an excellent candidate for reliable oil–water separation and humidity control applications, with notable improvements in antifouling performance.