Microstructure and magnetic properties of CoPt-SiNx∕Ag thin films
View through CrossRef
Different amounts of amorphous SiNx nonmagnetic material and magnetic Co50Pt50 alloy were cosputtered on the different thicknesses of Ag films at room temperature then annealed at different temperatures. When the thickness of Ag underlayer is 25nm, the CoPt∕Ag film has a minimum in-plane squareness (S∥) which is about 0.35. The out-of-plane squareness (S⊥), out-of-plane coercivity (Hc⊥), and saturated magnetization (Ms) values of the CoPt∕Ag (25nm) film are about 0.95, 15kOe, and 420emu∕cm3, respectively. From the microstructure analysis of CoPt-SiNx∕Ag (25nm) films with different volume percent of SiNx content, it is found that the average grain size of CoPt decreases from about 80to9nm when the volume percent of SiNx is increased from 0% to 50%. The S⊥, Hc⊥, and Ms values of the (CoPt)50-(SiNx)50∕Ag films are about 0.5, 7.5kOe, and 200emu∕cm3, respectively.
AIP Publishing
Title: Microstructure and magnetic properties of CoPt-SiNx∕Ag thin films
Description:
Different amounts of amorphous SiNx nonmagnetic material and magnetic Co50Pt50 alloy were cosputtered on the different thicknesses of Ag films at room temperature then annealed at different temperatures.
When the thickness of Ag underlayer is 25nm, the CoPt∕Ag film has a minimum in-plane squareness (S∥) which is about 0.
35.
The out-of-plane squareness (S⊥), out-of-plane coercivity (Hc⊥), and saturated magnetization (Ms) values of the CoPt∕Ag (25nm) film are about 0.
95, 15kOe, and 420emu∕cm3, respectively.
From the microstructure analysis of CoPt-SiNx∕Ag (25nm) films with different volume percent of SiNx content, it is found that the average grain size of CoPt decreases from about 80to9nm when the volume percent of SiNx is increased from 0% to 50%.
The S⊥, Hc⊥, and Ms values of the (CoPt)50-(SiNx)50∕Ag films are about 0.
5, 7.
5kOe, and 200emu∕cm3, respectively.
Related Results
Alternative Entrances: Phillip Noyce and Sydney’s Counterculture
Alternative Entrances: Phillip Noyce and Sydney’s Counterculture
Phillip Noyce is one of Australia’s most prominent film makers—a successful feature film director with both iconic Australian narratives and many a Hollywood blockbuster under his ...
Desarrollo de nuevas estructuras laminares de nanocelulosa con propiedades avanzadas para el packaging
Desarrollo de nuevas estructuras laminares de nanocelulosa con propiedades avanzadas para el packaging
(English) Changes in the use of raw materials and major lifestyle changes in first world societies have driven the massive use of petroleum-based materials in a wide range of appli...
Spray Coated Nanocellulose Films Productions, Characterization and Application
Spray Coated Nanocellulose Films Productions, Characterization and Application
Nanocellulose (NC) is a biodegradable, renewable and sustainable material. It has strong potential to use as a functional material in various applications such as barriers, coating...
Magnetic Properties of Electrodeposited Cobalt-Platinum (CoPt) and Cobalt-Platinum-Phosphide (CoPtP) Thin Films
Magnetic Properties of Electrodeposited Cobalt-Platinum (CoPt) and Cobalt-Platinum-Phosphide (CoPtP) Thin Films
CoPt and CoPtP thin films were synthesized using direct current (DC) aqueous electrodeposition from weak alkaline solutions. The basic plating solutions of binary CoPt thin films c...
Surface roughness and residual stress evolution in SiNx/ SiO2 multilayer coatings deposited by reactive pulsed magnetron sputtering
Surface roughness and residual stress evolution in SiNx/ SiO2 multilayer coatings deposited by reactive pulsed magnetron sputtering
The surface roughness and residual stress behavior in two types of SiNx/SiO2 dielectric quarter-wave stacks was investigated experimentally. A reactive pulsed magnetron sputtering ...
Magnetic Properties of CoPt Alloy Films Sputtered on Pt Underlayers
Magnetic Properties of CoPt Alloy Films Sputtered on Pt Underlayers
CoPt alloy films have been sputtered on room-temperature glass slides. It has been found that effective perpendicular anisotropy K
⊥ depends on the film compositi...
Magnetic cloak made of NdFeB permanent magnetic material
Magnetic cloak made of NdFeB permanent magnetic material
In the past few years, the concept of an electromagnetic invisibility cloak has received much attention. Based on the pioneering theoretical work, invisibility cloaks have been gre...
Diary of a Film Reviewer
Diary of a Film Reviewer
All critics declare not only their judgment of the work but also their claim to the right to talk about it and judge it. In short, they take part in...