Characterization of the Electron Beam Curing of Cationic Polymerization of Diglycidylether of Bisphenol A Epoxy Resin

The characterization of electron beam (E-beam) curing of diglycidyl-ether of bisphenol A-diaryliodonium hexafluoroantimonate epoxy resin-initiator system is reported as a function of (i) diaryliodonium hexafluoroantimonate catalyst (initiator) concentrations of 0.1-10 parts per hundred (phr) and (ii) total electron beam doses of 5-150 kilogray (kGy). The in situ E-beam temperature of the resin is monitored as a function of dose-time characteristics. The degree of cure is monitored after radiation exposure by Fourier transform infrared spectrometry (FTIR) and the glass transition temperatures (T g ) by differential scanning calorimetry (DSC). The degree of cure and cure rate increased with total dose exposure and initiator concentration. The maximum cure rate occurred at 5 kGy exposure and, thereafter, decreased as reactive species concentration decreased. The maximum in situ E-beam temperature of 76°C was recorded for the resin containing 10 phr of initiator, with a maximum degree of cure of 94% and a glass transition temperature of 86 C, indicating that the cure reactions under E-beam are glassy state diffusion controlled. The resin glass transition temperatures are considerably lower than the thermally cured glass transition temperatures of 170 C because of H 2 O termination reactions at the lower E-beam cure temperatures that result in a poor cross-linked network. In addition, the diaryliodonium hexafluoroantimonate catalytic activity for epoxide cationic polymerization is retarded by H 2 O. E-beam exposure causes the diaryliodonium hexafluoroantimonate to dissociate into active catalytic species, such as HSbF 6 , well below 100°C compared to catalytic thermal induced dissociation near 200°C. The E-beam cure reaction rate is modeled as a function of degree of cure and dose exposure by a standard autocatalytic kinetic model.