Influence of Partial Replacement of Nickel by Nitrogen on Microstructure and Mechanical Properties of Austenitic Stainless Steel

A new modified austenitic stainless steel has been developed through partial replacement of nickel by nitrogen. Nitrogen stainless steel was produced in 10 kg induction furnace under nitrogen pressure, while reference one, AISI 316 steel grade, was produced in open-induction furnace. Both were cast and hot forged, and the total nitrogen was determined. Furthermore, the produced forged steels were subjected to solution treatment at different temperatures. The microstructure of produced stainless steels was observed. The X-ray diffractmeter and Mossbauer effect spectroscopy were used to follow the phase change in reference and modified steels after different heat treatment temperatures. The influence of grain-size, soluble, and insoluble nitrogen on tensile strength and hardness was investigated. The major phase in the modified steel has a fcc structure similar to the reference one, but with finer grains and more expanded lattice. The yield strength and hardness of the nitrogen-modified stainless steel are higher than the reference steel. On the other hand, the increase of nitrogen content deteriorates the steel ductility.