A phase-field framework for anisotropic viscoelastic-viscoplastic fracture in short fiber-reinforced polymers in hygrothermal environments

This work presents a comprehensive phase-field framework for modeling anisotropic viscoelastic-viscoplastic fracture in short fiber-reinforced polymer (SFRP) composites under hygrothermal environments at finite deformation. The constitutive model employs a multiplicative decomposition of the deformation gradient into viscoelastic and viscoplastic components. An anisotropic phase-field formulation is developed using structural tensors to capture orientation-dependent fracture energy induced by multiple fiber families. Hygrothermal effects are incorporated through moisture-dependent swelling, thermal expansion, and temperature- and moisture-sensitive material parameters within the coupled framework. Numerical investigations demonstrate the framework's capability to capture complex fracture phenomena in SFRPs. Results reveal that fiber orientation fundamentally governs the spatial distribution of crack driving force, with maximum energy accumulation along fiber directions persisting throughout viscous relaxation. The anisotropy parameter controlling directional fracture resistance significantly influences crack path deflection. Hygrothermal degradation substantially reduces both peak load and fracture energy, with moisture absorption and elevated temperature each contributing to decreased mechanical performance. The framework captures the influence of fiber mechanical properties on global load-bearing capacity and crack propagation resistance. This unified computational framework advances the predictive modeling of damage evolution in SFRPs subjected to realistic environmental and mechanical loading conditions.