Effect of Ti 3 SiC 2 mass fraction on microstructure and tribological performance of laser cladded NiCr coating at high temperature

Purpose This paper aims to investigate the effect of Ti 3 SiC 2 on the high-temperature tribological behaviors of NiCr coating, which was beneficial to improve the friction-wear performance of hot work mold. Design/methodology/approach NiCr-Ti 3 SiC 2 coatings were prepared on H13 steel substrate by laser cladding. The microstructure, phases and hardness of obtained coatings were analyzed using a super-depth of field microscope, X-ray diffraction and microhardness tester, respectively, and the tribological performance of obtained coatings at 500°C was investigated using a high-temperature tester. Findings The results show the NiCr-Ti 3 SiC 2 coatings are comprised of γ-Ni solid, solution, Ti x Ni y , TiC and Ti 3 SiC 2 phases, and the coating hardness is increased with the increase of Ti 3 SiC 2 mass fraction, which is contributed to the fine-grain and dispersion strengthening effect by the addition of Ti 3 SiC 2 . The NiCr-Ti 3 SiC 2 coatings present excellent friction reduction and wear resistance by the synergetic action of Ti 3 SiC 2 lubricant and hard phase, and the wear mechanism is predominated by abrasive wear and oxidation wear. Originality/value Ti 3 SiC 2 phase was used to reinforce the tribological performance of H13 steel at high temperature, and the roles of friction reduction and wear resistance were discussed. Peer review The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2023-0004/