Thermal Intumescent Characteristics of Heated Sodium Silicate
View through CrossRef
A fire barrier material is made of a rubber in which intumescent materials are mixed. Sodium silicate is one of the intumescent materials which intumesces at low temperature. In this report, the thermal intumescent characteristics of water glass and sodium metasilicate are investigated. Thermal intumescent ratio of water glass and sodium metasilicate were measured using a thermo-gravimetry (TG/DTA) with the heating rate in the range from 1 K/min to 99.9 K/min. As the result, it is clarify that thermal intumescent characteristics depend on the heating rate. Thermal intumescent ratio increases with increasing the heating rate. No intumescence was observed under the condition that the heating rate ranges from 1 K/min to 20 K/min.
Title: Thermal Intumescent Characteristics of Heated Sodium Silicate
Description:
A fire barrier material is made of a rubber in which intumescent materials are mixed.
Sodium silicate is one of the intumescent materials which intumesces at low temperature.
In this report, the thermal intumescent characteristics of water glass and sodium metasilicate are investigated.
Thermal intumescent ratio of water glass and sodium metasilicate were measured using a thermo-gravimetry (TG/DTA) with the heating rate in the range from 1 K/min to 99.
9 K/min.
As the result, it is clarify that thermal intumescent characteristics depend on the heating rate.
Thermal intumescent ratio increases with increasing the heating rate.
No intumescence was observed under the condition that the heating rate ranges from 1 K/min to 20 K/min.
Related Results
Silicate application decreased methane emission from paddy soil under elevated UV‐B radiation
Silicate application decreased methane emission from paddy soil under elevated UV‐B radiation
AbstractA pot experiment was conducted to investigate the effects of silicate application quantity and silicate fertilizer type on rice growth and methane (CH4) emission under elev...
Femtosecond laser LenSx–assisted phacoemulsification of mature intumescent cataract
Femtosecond laser LenSx–assisted phacoemulsification of mature intumescent cataract
Background: Phacoemulsification (phaco) of mature intumescent cataract is one of the most difficult to perform anterior eye surgeries. In mature intumescent cataract phaco, the mos...
Thermal Effects in High Compactness CEA Stack
Thermal Effects in High Compactness CEA Stack
Thermal management is a pivotal aspect of stack durability and system operability. Consequently, understanding the thermal mapping within a stack based on its operating conditions ...
Effect of Long-Term Storage of Silicate Brick in Water on its Strength
Effect of Long-Term Storage of Silicate Brick in Water on its Strength
The article is devoted to the study of long-term storage of silicate brick in stationary water conditions on its strength and phase composition. The relevance of these studies is d...
Investigation of the hydration process and biological activity of a novel nanosilver incorporated dicalcium silicate based retrograde filling material
Investigation of the hydration process and biological activity of a novel nanosilver incorporated dicalcium silicate based retrograde filling material
Background
Although several materials have been used for retrograde filling following apical surgeries, there is no consensus on a single best material. Tricalcium s...
An Experimental Study of the Effects of Crack and Detachment on Insulation Properties of Intumescent Coating
An Experimental Study of the Effects of Crack and Detachment on Insulation Properties of Intumescent Coating
AbstractThis paper presents the results of an experimental study to investigate the failure modes of intumescent coatings and their effects on temperatures attained in steel sectio...
Expanded Polystyrene Beads Coated with Intumescent Flame Retardant Material to Achieve Fire Safety Standards
Expanded Polystyrene Beads Coated with Intumescent Flame Retardant Material to Achieve Fire Safety Standards
The compatibility and coating ratio between flame retardant materials and expanded polystyrene (EPS) foam is a major impediment to achieving satisfactory flame retardant performanc...
Near-Surface Properties of Europa Constrained by the Galileo PPR Measurements
Near-Surface Properties of Europa Constrained by the Galileo PPR Measurements
NASA's Europa Clipper mission will characterize the current and recent surface activity of the icy-moon Europa through a wide range of remote sensing observations. In particular, t...