Failure mechanism and acoustic emission signal characteristics of coatings under the condition of impact indentation
View through CrossRef
Abstract
In this work, the substrate, NiCr coating, Al2O3 coating with NiCr undercoating and Al2O3 coating were tested by an impact indentation device equipped with an acoustic emission (AE) detection equipment. The surface morphology, dimension, cross-sectional image, 3D topography of indention and bonding strength of coatings were analyzed. The failure mechanism and AE signal characteristics of the coatings under impact were studied. The results demonstrate that the failure mode of NiCr coating was dominated by interface cracking, and that of Al2O3 coating is fracture and accompanied by a small amount of interface cracking, while Al2O3 coating with NiCr undercoating possesses common characteristics of the first two. The energy counting and wave voltage of AE signal were more sensitive to the bonding strength of coating in the impact process, which can be used to characterize the bonding strength of coating.
Walter de Gruyter GmbH
Title: Failure mechanism and acoustic emission signal characteristics of coatings under the condition of impact indentation
Description:
Abstract
In this work, the substrate, NiCr coating, Al2O3 coating with NiCr undercoating and Al2O3 coating were tested by an impact indentation device equipped with an acoustic emission (AE) detection equipment.
The surface morphology, dimension, cross-sectional image, 3D topography of indention and bonding strength of coatings were analyzed.
The failure mechanism and AE signal characteristics of the coatings under impact were studied.
The results demonstrate that the failure mode of NiCr coating was dominated by interface cracking, and that of Al2O3 coating is fracture and accompanied by a small amount of interface cracking, while Al2O3 coating with NiCr undercoating possesses common characteristics of the first two.
The energy counting and wave voltage of AE signal were more sensitive to the bonding strength of coating in the impact process, which can be used to characterize the bonding strength of coating.
Related Results
Calculation of the depth of rope-tightening soft material and analysis of its relationship with the tightening force
Calculation of the depth of rope-tightening soft material and analysis of its relationship with the tightening force
To analyze the relationship between the tension force of a rope and the bundled material's indentation, a model of tightening by rope for soft material was designed for testing. By...
Optimising tool wear and workpiece condition monitoring via cyber-physical systems for smart manufacturing
Optimising tool wear and workpiece condition monitoring via cyber-physical systems for smart manufacturing
Smart manufacturing has been developed since the introduction of Industry 4.0. It consists of resource sharing and networking, predictive engineering, and material and data analyti...
Research on Acoustic Emission Source Localization Technology Based on AI Deep Learning
Research on Acoustic Emission Source Localization Technology Based on AI Deep Learning
Acoustic emission source localization is the basic function of the application of acoustic emission technology. For complex structures, mathematical analysis positioning algorithms...
Mechanism and numerical simulation of electromagnetic acoustic emission based on short-time pulse and large current
Mechanism and numerical simulation of electromagnetic acoustic emission based on short-time pulse and large current
Abstract
To address the issue of traditional acoustic emission detection of tank bottom plate defects, which requires external force induction and exhibits low detec...
Clustering Analysis of Acoustic Emission Signals Based on Unsupervised Deep Learning
Clustering Analysis of Acoustic Emission Signals Based on Unsupervised Deep Learning
In order to improve the automation degree of detecting and determining the damage types of metal structures by acoustic emission signals, starting from the acoustic emission charac...
PROTECTIVE ABILITY OF TIN-NICKEL COATINGS
PROTECTIVE ABILITY OF TIN-NICKEL COATINGS
The calculation of the corrosion current of the steel – plating allowed us to estimate the protective properties and the porosity of the Tin-Nickel coatings. Measured in 3% NaCl so...
Investigations of Surface-Treated Wood by a Micro-Indentation Approach: A Short Review and a Case Study
Investigations of Surface-Treated Wood by a Micro-Indentation Approach: A Short Review and a Case Study
Over the past 50 years, instrumented indentation, in which an indenter tip probes the specimen surface with a regulated force and displacement to characterize its mechanical proper...
Strain-Induced Cracking Behavior of Coating/Substrate Systems and Strain Tolerant Design for Thick Coatings
Strain-Induced Cracking Behavior of Coating/Substrate Systems and Strain Tolerant Design for Thick Coatings
The life span for a coating attached to its substrate is basic support for their desired protective function. Therefore, it is necessary to find out the causes responsible for the ...