NaOH Molarity's Impacts on SCGC's Workability and Durability with Ecologically Friendly Industrial By-Products
View through CrossRef
The objective of the analysis is to investigate the workability and durability properties of self-compacting geopolymer concrete (SCGC) based on fly ash and GGBS on various NaOH molarities. A system of trial and error was employed to achieve the SCGC mix ratio. By conducting workability properties test such as slump flow, T50 slump flow, V-funnel, and L-box and At 28, 56 and 90 days, durability properties such as water absorption, sulphuric acid attack and sorptivity were tested. The specimens have been cured for 24 hours in the oven at 70 ° C, and environmental healing is accompanied by the test days respectively. For all the molarities including 8, 10 and 12 M with a constant binding content of 400 kg / m3, the fly ash mass fraction was changed by GGBS by 0, 30, 50, and 70 per cent by weight. In all molarities, the fluid to binder ratio of 0.47 by mass has been kept constant and the S.P dosage has remained consistent with 0% replacement and 4% with 30, 50 and 70% replacement and the water content has therefore changed accordingly. The experimental result showed lower workability parameters such as slump flow and L-box ratios with increased molarity and GGBS content, increased T50 slump flow and increased V-Funnel with increased molarity and GGBS content, and the whole study was performed as suggested by the EFNARC guidelines. Durability properties such as water absorption and sorptiveness have shown good resistance with an increase of the GGBS content and an increase in molarity. Seventy percent fly-ash replacement by GGBS showed more strength degradation when held at 5percent concentration in the sulphuric acid medium. Hence SCGC can be a better replacement for normal OPC concrete both in terms of strength and durability with reduced CO2 emission.
Blue Eyes Intelligence Engineering and Sciences Engineering and Sciences Publication - BEIESP
Title: NaOH Molarity's Impacts on SCGC's Workability and Durability with Ecologically Friendly Industrial By-Products
Description:
The objective of the analysis is to investigate the workability and durability properties of self-compacting geopolymer concrete (SCGC) based on fly ash and GGBS on various NaOH molarities.
A system of trial and error was employed to achieve the SCGC mix ratio.
By conducting workability properties test such as slump flow, T50 slump flow, V-funnel, and L-box and At 28, 56 and 90 days, durability properties such as water absorption, sulphuric acid attack and sorptivity were tested.
The specimens have been cured for 24 hours in the oven at 70 ° C, and environmental healing is accompanied by the test days respectively.
For all the molarities including 8, 10 and 12 M with a constant binding content of 400 kg / m3, the fly ash mass fraction was changed by GGBS by 0, 30, 50, and 70 per cent by weight.
In all molarities, the fluid to binder ratio of 0.
47 by mass has been kept constant and the S.
P dosage has remained consistent with 0% replacement and 4% with 30, 50 and 70% replacement and the water content has therefore changed accordingly.
The experimental result showed lower workability parameters such as slump flow and L-box ratios with increased molarity and GGBS content, increased T50 slump flow and increased V-Funnel with increased molarity and GGBS content, and the whole study was performed as suggested by the EFNARC guidelines.
Durability properties such as water absorption and sorptiveness have shown good resistance with an increase of the GGBS content and an increase in molarity.
Seventy percent fly-ash replacement by GGBS showed more strength degradation when held at 5percent concentration in the sulphuric acid medium.
Hence SCGC can be a better replacement for normal OPC concrete both in terms of strength and durability with reduced CO2 emission.
Related Results
Decoration and Durability: Ornaments and their ‘appropriateness’ from fashion and design to architecture
Decoration and Durability: Ornaments and their ‘appropriateness’ from fashion and design to architecture
<p>Throughout the scales of design there has been an exploding interest in the ornament that seems to be fuelled by different kinds of digital technology and media from CAD t...
Industrial Symbiosis: An Exploration of the Potential of Sustainable Waste Management in the UAE
Industrial Symbiosis: An Exploration of the Potential of Sustainable Waste Management in the UAE
This study aims to provide targeted policy pathways supporting the emergence of industrial symbiosis in practice within the UAE. The introduction provides an overview of state-of-t...
Building industrial-education partnerships in acoustics
Building industrial-education partnerships in acoustics
Strong industry relations can provide many positive impacts for an educational program. The rewards of such an educational-industrial partnership only occur after the hard work of ...
A Novel Recycling Technology of Bamboo Using NaOH
A Novel Recycling Technology of Bamboo Using NaOH
The bamboo industry in Japan is declined, and disordered bamboo forests are increasing. Although maintenance of bamboo forest is needed, a large amount of bamboo wastes after loggi...
Analyzing the Impact of Supplementary Cementitious Material and Polypropylene Fiber on the Fresh, Mechanical Properties, and Acid Attack of Quaternary Blended Self Compacting Concrete
Analyzing the Impact of Supplementary Cementitious Material and Polypropylene Fiber on the Fresh, Mechanical Properties, and Acid Attack of Quaternary Blended Self Compacting Concrete
Self-Compacting Concrete (SCC) is defined as concrete that has an ability to flow under its own weight, to fill the required space or formwork completely and to produce a dense and...
Cardboard Architecture
Cardboard Architecture
Explorations in the use of cardboard products in architecture exist since the 1940s. However, it was not until the early 1990s, when Shigeru Ban's work emerged when cardboar...
DURABLE GOODS
DURABLE GOODS
ABSTRACTIn his thoughtful discussion of what makes some historical texts durable, lasting through time, Jaume Aurell arrives at the conclusion that these works show a balance betwe...
Synthesis of Glucopyranosyl Acetic from Sago Flour as Raw Material for the Synthetic Polymers
Synthesis of Glucopyranosyl Acetic from Sago Flour as Raw Material for the Synthetic Polymers
Synthesis of glucopyranosyl acetic from sago flour as raw material for the synthetic polymers has been successfully carried out. The synthesis product is obtained through two react...