Impact of In doping on GeTe phase-change materials thin films obtained by means of an innovative plasma enhanced metalorganic chemical vapor deposition process

We investigated the deposition and the phase-change properties of In-doped GeTe thin films obtained by plasma enhanced metalorganic chemical vapor deposition and doped with indium using a solid delivery system. The sublimated indium precursor flow rate was calculated as a function of sublimation and deposition parameters. Indium related optical emission recorded by means of optical emission spectroscopy during deposition plasma allowed proposing the dissociation mechanisms of the [In(CH3)2N(CH3)2]2 solid precursor. In particular, using an Ar + H2 + NH3 deposition plasma, sublimated indium molecules are completely dissociated and do not induce by-product contamination by addition of nitrogen or carbon in the films. X-ray photoelectron spectroscopy evidences the formation of In-Te bonds in amorphous as-deposited In-doped GeTe films. The formation of an InTe phase after 400 °C annealing is also evidenced by means of X-ray diffraction analysis. The crystallization temperature Tx, deduced from monitoring of optical reflectivity of In-doped GeTe films with doping up to 11 at. % slightly varies as a function of the In dopant level with a decrease of Tx down to a minimum value for an In doping level of about 6–8 at. %. In this In doping range, the structure of crystallized In-GeTe films changes and is dominated by the presence of a crystalline In2Te3 phase. Finally, the Kissinger activation energy for crystallization Ea is showing to monotonically decrease as the indium content in the GeTe film is increased indicating a promising effect of In doping on crystallization speed in memory devices while keeping a good thermal stability for data retention.