In order to improve the wear resistance of offshore drilling equipment, CoCrFeNiMn high-entropy alloy coatings were prepared by cold spraying (CS) and high-speed oxygen fuel spraying (HVOF), and the coatings were subjected to vacuum heat treatment at different temperatures (500 °C, 700 °C and 900 °C). The friction and wear experiments of the coatings before and after vacuum heat treatment were carried out in simulated seawater drilling fluid. The results show that CoCrFeNiMn high-entropy alloy coatings prepared by CS and HVOF have dense structure and bond well with the substrate. After vacuum heat treatment, the main peaks of all oriented FCC phases are broadened and the peak strength is obviously enhanced. The two types of coatings achieve maximum hardness after vacuum heat treatment at 500 °C; the Vickers microhardness of CS-500 °C and HVOF-500 °C are 487.6 and 352.4 HV0.1, respectively. The wear rates of the two coatings at room temperature are very close. CS and HVOF coatings both have the lowest wear rate after vacuum heat treatment at 500 °C. The CS-500 °C coating has the lowest wear rate of 0.2152 mm3 m−1 N−1, about 4/5 (0.2651 mm3 m−1 N−1) of the HVOF-500 °C coating. The wear rates and wear amounts of the two coatings heat-treated at 700 °C and 900 °C decrease due to the decrease in microhardness. The wear mechanisms of the coatings before and after vacuum heat treatment are adhesive wear, abrasive wear, fatigue wear and oxidation wear.
Title: Microstructure and Corrosive Wear Properties of CoCrFeNiMn High-Entropy Alloy Coatings
Description:
In order to improve the wear resistance of offshore drilling equipment, CoCrFeNiMn high-entropy alloy coatings were prepared by cold spraying (CS) and high-speed oxygen fuel spraying (HVOF), and the coatings were subjected to vacuum heat treatment at different temperatures (500 °C, 700 °C and 900 °C).
The friction and wear experiments of the coatings before and after vacuum heat treatment were carried out in simulated seawater drilling fluid.
The results show that CoCrFeNiMn high-entropy alloy coatings prepared by CS and HVOF have dense structure and bond well with the substrate.
After vacuum heat treatment, the main peaks of all oriented FCC phases are broadened and the peak strength is obviously enhanced.
The two types of coatings achieve maximum hardness after vacuum heat treatment at 500 °C; the Vickers microhardness of CS-500 °C and HVOF-500 °C are 487.
6 and 352.
4 HV0.
1, respectively.
The wear rates of the two coatings at room temperature are very close.
CS and HVOF coatings both have the lowest wear rate after vacuum heat treatment at 500 °C.
The CS-500 °C coating has the lowest wear rate of 0.
2152 mm3 m−1 N−1, about 4/5 (0.
2651 mm3 m−1 N−1) of the HVOF-500 °C coating.
The wear rates and wear amounts of the two coatings heat-treated at 700 °C and 900 °C decrease due to the decrease in microhardness.
The wear mechanisms of the coatings before and after vacuum heat treatment are adhesive wear, abrasive wear, fatigue wear and oxidation wear.
Related Results
Effects of different factors on the friction and wear mechanical properties of titanium alloy materials with cortical bones at near service conditions
Effects of different factors on the friction and wear mechanical properties of titanium alloy materials with cortical bones at near service conditions
Abstract
Artificial joint is one of the most effective methods to treat joint injuries. The service performance of artificial joints is gradually bad due to the wear of art...
Corrosive wear and electrochemical corrosion behaviors of laser thermal sprayed CoCrAlYTaSi coatings in 3.5 Wt.% NaCl solution
Corrosive wear and electrochemical corrosion behaviors of laser thermal sprayed CoCrAlYTaSi coatings in 3.5 Wt.% NaCl solution
Purpose
This paper aims to enhance the corrosive wear and electrochemical corrosion of Ti–6Al–4V alloy.
Design/methodology/approach
A CoCrAlYTaSi alloy coating was fabricated on ...
Microstructure, Mechanical Properties, and Friction-Wear Mechanisms of NbMoTaWV Refractory High-Entropy Alloy Coatings Fabricated via Laser Cladding
Microstructure, Mechanical Properties, and Friction-Wear Mechanisms of NbMoTaWV Refractory High-Entropy Alloy Coatings Fabricated via Laser Cladding
In this study, NbMoTaWV RHEA coatings were fabricated via laser cladding, and X-ray diffraction (XRD), scanning electron microscopy equipped with energy-dispersive X-ray spectrosco...
Molecular dynamics simulation of size dependent plastic deformation mechanism of CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloys
Molecular dynamics simulation of size dependent plastic deformation mechanism of CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloys
Recently proposed crystalline/amorphous dual-phase high-entropy alloy is an effective strategy to obtain high-entropy, high-strength and high-toughness alloys. And the relative pla...
Strengthening mechanism and wear behavior of AlCrFeNiNb<sub><i>x</i></sub> high-entropy alloys from the perspective of phase modulation
Strengthening mechanism and wear behavior of AlCrFeNiNb<sub><i>x</i></sub> high-entropy alloys from the perspective of phase modulation
AlCoCrFeNi high-entropy alloys have consistently attracted attention due to their outstanding strength-to-ductility ratio. However, the substantial content of expensive cobalt in t...
Wear-resistant Coatings on Aluminum Alloys
Wear-resistant Coatings on Aluminum Alloys
Aluminum alloys are widely used in industry. Recently, they are used as a replacement for steel for the manufacture of pulleys, gears, columns of hydraulic rotary transmissions of ...
Micro-Structures and High-Temperature Friction-Wear Performances of Laser Cladded Cr–Ni Coatings
Micro-Structures and High-Temperature Friction-Wear Performances of Laser Cladded Cr–Ni Coatings
Cr–Ni coatings with the mass ratios of 17% Cr–83% Ni, 20% Cr–80% Ni and 24% Cr–76% Ni were fabricated on H13 hot work mould steel using a laser cladding (LC). The surface–interface...
Improved organic coating delamination resistance using physical vapour deposited Zn-Mg layers on strip steel
Improved organic coating delamination resistance using physical vapour deposited Zn-Mg layers on strip steel
Physical vapour deposition (PVD) of zinc alloy coatings was investigated as a potential substitute process for commercially available hot dip galvanising (HDG) of strip steel. Ther...