Pea Pod–Derived Biochar–Zeolitic Imidazolate Framework Composite for the Photocatalytic Degradation of Two Organic Dyes Crystal Violet and Victoria Blue

ABSTRACT The rapid increase of water pollution globally is a vital environmental concern that requires the immediate attention of researchers to find new innovative ways to remove unwanted environmental pollutants from our water sources. With the advances in the field of sustainable engineering, there is a high demand for the effective utilization of biomass resources for the removal of aqueous environmental contaminants. Biochar is carbon carbon‐enriched substance obtained by biomass pyrolysis; it is inexpensive and has received wide attention in the field of wastewater treatment. Herein, we describe the synthesis of pea pod (PO) biochar‐reinforced zeolitic imidazolate framework (ZIF‐8) nanocomposite (PO@ZIF‐8) through the in situ precipitation of ZIF‐8 onto the biochar surface. The crystal growth, morphology, chemical composition, and optical characteristics of fabricated PO@ZIF‐8 nanocomposite were scrutinized through PXRD, SEM, TEM, UV‐DRS, PL, and XPS analysis. The dodecahedral‐shaped PO@ZIF‐8 particles have an average size between 140 and 160 nm. The biochar‐reinforced ZIF‐8 nanocomposite showed significantly higher photocatalytic activity than the pure ZIF‐8 for the degradation of two commonly found organic dyes crystal violet (CV) and Victoria Blue (VB) in the presence of direct sunlight irradiation. The PO@ZIF‐8 nanocomposite showed the highest degradation efficiency of ~87% and ~80% within 50 min of irradiation time at a catalyst dosage of 20 mg for 30 ppm CV and VB dye solutions at pH 8. First‐order kinetics were obeyed during the photodegradation with 0.041 and 0.030 min −1 as the constant of degradation for the removal of CV and VB. The radical scavenger experiment and the photoluminescence analysis confirm the active participation of ·OH radical in the degradation of both dyes. LC–MS and TOC analysis was also performed to determine the degradation products and for evaluation of the degradation progress. Moreover, the synthesized PO@ZIF‐8 composite also exhibit good stability till the fourth cycle with high degradation efficiency thus making it a good choice of catalyst in the field of environmental decontamination.