Utilization of Red Mud from Processing of Low-Quality Bauxites

Red mud from bauxite processing is among the large-tonnage technogenic waste that poses a significant ecological threat. At the same time, red mud serves as a raw material source for expanding the resource base for obtaining iron, rare metals, and rare earth elements. Numerous studies on their utilization have shown that only through comprehensive processing, combining pyrometallurgical and hydrometallurgical methods, is it possible to maximize the extraction of all the useful components. This work addresses the first stage of a comprehensive technology for processing red mud through reduction smelting, separating iron in the form of pig iron, and producing slag. Studies were conducted on the reductive smelting of red mud using waste slurry from alumina production as the calcium-containing material, taken in proportions calculated to obtain a fluid slag with a hydraulic modulus of 0.55–0.8. The permissible mixing range of red mud with waste slurry was determined to be in the ratio of 0.56–1.2. In cases where the charge was prepared in violation of the required hydraulic modulus value, pig iron was not obtained during smelting. When the hydraulic modulus requirement was met, the temperature of the reductive smelting process was 1350–1400 °C. The total amount of recovered iron obtained as pig iron and fine fractions amounted to 99.5% of the original content. The low iron content (0.23–0.31%) in the non-magnetic slag fraction allows for the production of high-quality titanium oxide and rare earth element concentrates in the subsequent stages of the comprehensive hydrometallurgical processing of red mud, involving acid leaching. Based on the results of a phase analysis of the slag, pig iron, and melt, the reactions of the reductive smelting process were established, and their thermodynamic likelihood was determined. In fluid slags, the content of the sodium aluminosilicate phase is twice as high as that in slag with a higher hydraulic modulus. The reductive smelting of 100% red mud with the addition of calcium oxide, calculated to achieve a hydraulic module of 0.55 at a temperature of 1350–1400 °C, produced pig iron and slag with high alkali and iron contents.