Effect of crosslinking agents on the strength characteristics of cellulosic fabrics using 23 32 mixed level factorial

Purpose Low pilling and wrinkle-free appearance of cellulosic fabrics are always demanded. Resin finishes are applied to improve these properties, but there is an adverse effect of the resin finish as it tends to reduce the strength of the fabrics. Therefore, the effect of the two most important finishes; anti-pilling and resin finish, on the strength characteristics of 100% viscose and 50:50 Viscose/cotton plain and satin fabrics were investigated in this paper. The purpose of this study is to identify significant factors affecting the strength of fabrics finished with crosslinking agents [non-ionic acrylate copolymer and (dimethyloldihydroxyethyleneurea)]. Design/methodology/approach A statistical model of 23 32 mixed level factorial design was used for the study. Appratan N9211 (A) and Arkofix NF (B) were tested at three concentrations, whereas three factors fabric; weave (C), blend ratio (D) and curing method (E) were tested at two levels. The performance of the finish was evaluated by two response variables, which were tensile and tear strength. Findings The various conditions of high strength values of the fabrics were presented in this paper. It was found that the tear strength of the fabrics increased after finishing except for 50:50 viscose/cotton plain fabric, whereas the tensile strength of plain fabrics is better at shock cure and for a satin normal cure is better. The model adequacy plots exhibit that the assumptions of normality and independence are not desecrated. Moreover, the values of “predicted R2” are in reasonable agreement with the “adjusted R2,” which confirms that models have been accounted for most of the inconsistency. Originality/value This paper is a part of my PhD dissertation. Unlike the previous studies, this paper investigated the effect of two crosslinking agents, Appretan N9211 as anti-pilling and Arkofix NF as wrinkle resistant agents on 100% viscose and 50:50 viscose/cotton plain and satin. Three different concentrations of both the crosslinking agents were used. Also, fixation of the finishes was carried out at a normal cure and shock cure.