Effect of Torrefaction on the Physiochemical Properties of White Spruce Sawdust for Biofuel Production

Torrefaction pretreatment is a mild form of pyrolysis that has the potential to produce a high-quality raw material for making biofuel that serves as a replacement for coal in the bioenergy industry. Microwave-assisted torrefaction was conducted on white spruce sawdust (WSS) at temperatures of 200 °C, 250 °C, and 300 °C and retention times of 5 min, 7 min, and 9 min in an inert environment. The torrefaction process produces a solid carbon, commonly known as biochar, and condensable (torrefaction liquid (TL)) and non-condensable gases. In this study, torrefaction characteristics were investigated to observe its effects on the thermal and physiochemical properties of the pellets produced. During the torrefaction process, a significant mass loss associated with the decomposition of hemicellulose was observed. The hemicellulose content drastically reduced to approximately 1.8% and the cellulose content was reduced by approximately 10%, while the lignin gained approximately 35% as the severity increased. This led to an improvement in the higher heating value (HHV), hydrophobicity, bulk, particle density, pellet dimensional stability, and pellet density. However, the pellet tensile strength decreased as the torrefaction severity increased. Pellet tensile strength is a critical indicator of biomass pellets that expresses the force required to crush or damage a pellet. Therefore, to enhance the tensile strength of the pellets, the introduction of a binder was necessary. Torrefaction liquid and sawdust were used as additives at different proportions during pelletization. The addition of binders (torrefaction liquid and sawdust) to the pellet formulation increased the tensile strength of the torrefied WSS by approximately 50%. The OH groups in the biomass break down to a limited degree due to dehydration. This hinders the formation of H bonds, thereby increasing the chances that the pretreated biomass will become hydrophobic. The SEM graphs showed that the torrefied WSS pellets demonstrated more firmly glued surfaces with fewer pores spaces when set side by side with the raw pellets. The thermogravimetric analysis conducted showed that the torrefaction of WSS slightly reduced its thermal stability.