Novel Functional Mesoporous Materials Obtained from Nanostructured Diblock Copolymers

AbstractSummary: Novel carboxy (COOH)‐functionalized mesoporous polystyrene membranes were prepared from polystyrene‐block‐poly(D,L‐lactide) (PS‐b‐PLA) diblock copolymers through the selective degradation of the PLA block. The combination of atom transfer radical polymerization (ATRP) and ring‐opening polymerization (ROP) techniques enabled the synthesis of nanostructured diblock copolymers possessing carboxylic acid functionality at the junction between both blocks. Such copolymers were subjected to shear flow through the use of a channel die to align their nanodomains. Under mild alkaline conditions, the quantitative hydrolysis of the polyester nanodomains afforded mesoporous materials with COOH‐coated pore walls. The PS‐b‐PLA precursors as well as the resulting porous systems were carefully analyzed by size exclusion chromatography (SEC), 1H NMR, scanning electron microscopy (SEM), and two‐dimensional small‐angle X‐ray scattering (2‐D SAXS). Moreover, the specific surface area and pore size distribution were determined by nitrogen sorption porosimetry.